As shown in Table 1, LCO raw material powder was prepared and was named powder A. The resultant LCO powder A (100 parts by weight), a dispersive medium (toluene:2-propanol=1:1) (100 parts by weight), a binder (polyvinyl butyral: Product No. BM-2, manufactured by Sekisui Chemical Co., Ltd.) (10 parts by weight), a plasticizer (di-2-ethylhexyl phthalate (DOP), manufactured by Kurogane Kasei Co., Ltd.) (4 parts by weight), and a dispersant (product name: RHEODOL SP-O30, manufactured by Kao Corporation) (2 parts by weight) were mixed. The resultant mixture was defoamed by stirring under reduced pressure to prepare an LCO slurry with a viscosity of 4000 cP. The viscosity was measured with an LVT viscometer manufactured by Brookfield. The slurry prepared was formed into an LCO green sheet onto a PET film by a doctor blade process. The dried thickness of the LCO green sheet was 240 μm.
(1b) Preparation of LCO Sintered Plate